Aluacero® panel range
Aluacero® panel 11 blind slats
| Material | Thickness (mm) |
Weight by linear metre (kg) | Weight by square metre (kg) | l (cm4/m) | W (cm3/m) | Punched Surface | Standard Finishings |
|---|---|---|---|---|---|---|---|
| Steel | 0,6 | 5,89 | 9,06 | 15,43 | 8,19 | NO | Cold Rolled Galvanized |
| Aluminium | 1,0 | 3,44 | 5,29 | 25,73 | 13,54 | NO | Raw |
Note: the dimensions and values provided on this web site are nominal values. There may be small differences due to material tolerances and the profiling process.
Aluacero® panel 11 slats with windows
| Material | Thickness (mm) |
Weight by linear metre(kg) | Weight by square metre (kg) | l (cm4/m) | W (cm3/m) | Punched surface | Standard Finishings |
|---|---|---|---|---|---|---|---|
| Steel | 0,6 | 4,85 | 7,46 | 14,96 | 7,88 | 22% | Cold Rolled Galvanized |
| Aluminium | 1,0 | 3,05 | 4,69 | 24,98 | 13,03 | 22% | Raw |
Note: the dimensions and values provided on this web site are nominal values. There may be small differences due to material tolerances and the profiling process.
Aluacero® Panel 11 micro-perforated slats
| Material | Thickness (mm) |
Weight by metre(kg) | Weight by square metre (kg) | l (cm4/m) | W (cm3/m) | Punched Surface | Standard Finishings |
|---|---|---|---|---|---|---|---|
| Steel | 0,6 | 5,42 | 8,34 | 14,96 | 4,96 | 11% | Cold Rolled Galvanized |
| Aluminium | 1,0 | 3,21 | 4,94 | 24,98 | 13,03 | 11% | Raw |
Note: the dimensions and values provided on this web site are nominal values. There may be small differences due to material tolerances and the profiling process.
Aluacero® panel 11 multi-perforated slats
| Material | Thickness (mm) |
Weight by linear metre(kg) | Weight by square metre (kg) | l (cm4/m) | W (cm3/m) | Punched Surface | Standard Finishings |
|---|---|---|---|---|---|---|---|
| Steel | 0,6 | 4,00 | 6,15 | 9,28 | 7,88 | 32% | Galvanized |
| Aluminium | 1,0 | 2,33 | 3,59 | 15,45 | 8,20 | 32% | Raw |
Note: the dimensions and values provided on this web site are nominal values. There may be small differences due to material tolerances and the profiling process.
Aluacero® panel 5 blind slats
| Material | Thickness (mm) |
Weight by linear metre(kg) | Weight by square metre (kg) | l (cm4/m) | W (cm3/m) | Punched Surface | Standard Finishings |
|---|---|---|---|---|---|---|---|
| Steel | 0,6 | 2,73 | 92,19 | 15,43 | 8,19 | NO | Cold Rolled Galvanized |
| Aluminium | 1,0 | 1,57 | 5,322 | 25,73 | 13,54 | NO | Raw |
Note: the dimensions and values provided on this web site are nominal values. There may be small differences due to material tolerances and the profiling process.
Aluacero® panel 5 slats with windows
| Material | Thickness (mm) |
Weight by linear metre (kg) | Weight by square metre (kg) | l (cm4/m) | W (cm3/m) | Punched Surface | Standard Finishings |
|---|---|---|---|---|---|---|---|
| Steel | 0,6 | 2,24 | 7,54 | 14,96 | 7,88 | 22% | Cold Rolled Galvanized |
| Aluminium | 1,0 | 1,38 | 4,68 | 24,98 | 13,03 | 22% | Raw |
Note: the dimensions and values provided on this web site are nominal values. There may be small differences due to material tolerances and the profiling process.
Aluacero® panel 5 micro-perforated slats
| Material | Thickness (mm) |
Weight by metre(kg) | Weight by square metre (kg) | l (cm4/m) | W (cm3/m) | Punched Surface | Standard Finishings |
|---|---|---|---|---|---|---|---|
| Steel | 0,6 | 2,51 | 8,45 | 14,96 | 4,96 | 11% | Cold Rolled Galvanized |
| Aluminium | 1,0 | 1,46 | 4,95 | 24,98 | 13,03 | 11% | Raw |
Note: the dimensions and values provided on this web site are nominal values. There may be small differences due to material tolerances and the profiling process.
Aluacero® panel 5 multi-perforated slats
| Material | Thickness (mm) |
Weight by linear metre(kg) | Weight by square metre (kg) | l (cm4/m) | W (cm3/m) | Punched Surface | Standard Finishings |
|---|---|---|---|---|---|---|---|
| Steel | 0,6 | 1,86 | 6,26 | 9,28 | 7,88 | 32% | Galvanized |
| Aluminium | 1,0 | 1,06 | 3,59 | 15,45 | 8,20 | 32% | Raw |
Note: the dimensions and values provided on this web site are nominal values. There may be small differences due to material tolerances and the profiling process.